Characteristics of the spontaneous deposition of Sn in polycrystalline Pt

Abstract

Spontaneous deposition of tin (Sn) in polycrystalline platinum (Pt pc) from a sulfuric acid solution of tin salts, was evaluated by conventional electrochemical techniques, to determine its characteristics. Tin was deposited from a solution of SnCl 2 or SnSO 4 in sulfuric acid 1 M. The degree of surface coating by Sn was calculated by evaluating the region of hydrogen electrosorption through voltammograms performed using solutions containing only the supporting electrolyte, and the supporting electrolyte containing the Sn salt, respectively. The adsorption behavior of tin and oxidation have been studied by the results obtained with platinum electrodes and electrodes of platinum/tin, considering as comparative parameter the adsorption efficiency with respect to the area free of platinum.

La deposición espontánea de estaño (Sn) en platino policristalino (Pt pc) a partir de una solución de ácido sulfúrico de sales de estaño, se evaluó mediante técnicas electroquímicas convencionales, para determinar sus características. El estaño se depositó a partir de una solución de SnCl 2 o SnSO 4 en ácido sulfúrico 1 M. El grado de recubrimiento de la superficie por Sn se calculó evaluando la región de electrosorción de hidrógeno a través de voltamogramas realizados utilizando soluciones que contienen solo el electrolito de soporte y el electrolito de soporte que contiene la sal Sn, respectivamente. El comportamiento de adsorción del estaño y la oxidación se ha estudiado mediante los resultados obtenidos con electrodos de platino y electrodos de platino / estaño, considerando como parámetro comparativo la eficiencia de adsorción con respecto al área libre de platino.