Internal bond strength of particle boards manufactured from a mixture of Gmelina arborea, Tectona grandis and Cupressus lusitanica with the fruit of Elaeis guineensis, leaves of Ananas comosus and tetra pak packages

Abstract

Abstract. Some countries with tropical climate produce a great variety of lignocellulosic waste from crops planted in small areas and also, urban areas produce a great amount of wastes from Tetra Paks packages without any kind of management. A possible solution is to incorporate these wastes into particleboards. The main objective of this work is to determine the relation in a mixture of particles from the empty fruit bunch of Elaeis guineensis (EFB), pineapple leaves (Ananas comosus) (PL), and Tetra Pak packages (TP) with 3 kinds of wood from forest plantations (Gmelina arborea, Tectona grandis and Cupressus lusitanica) commonly used for particleboards manufacturing. The proportions 50:50, 70:30, and 90:10 (waste:wood) with adhesive at 6, 8, and 10% (weight/weight) were tested for resistance regarding internal bond strength (IB). The results showed that the IB values varied from 100 to 275 kPa in matrixes with PL, from 100 to 360 kPa for EFB and from 200-600 kPa in matrixes with TP. Furthermore, it was found that when the EFB and PL proportion decreases, the IB values increased, where mixture 90:10 with 10% adhesive showed the highest IB values. But for matrixes with TP, IB value is higher in proportions where the presence of wastes is greater, the 50:50 proportion with 10% adhesive showed the highest strength.

Resumen. Algunos países con clima tropical producen una gran variedad desechos lignocelulósicos de cultivos plantados en pequeñas áreas y además los centros urbanos producen una cantidad de tetra pak package sin ningún tipo de manejo. El objetivo principal de este trabajo determinar la relación en una mezcla de partículas del fruto procesado de Elaeis guineensis (BPF), hojas de Ananas cumosos (LP) y empaques de tetra pak (TP) con 3 maderas de plantaciones forestales (Gmelina arborea, Tectona grandis and Cupressus lusitanica), comúnmente utilizadas en la fabricación de particleboards. Las proporciones de 50:50, 70:30 y 90:10 (residuo:madera) con adhesivo en 6, 8 y 10% (peso/peso) fueron probados su resistencia en cohesión interna (IB). Los resultados mostraron que los valores de IB variaron de 100 a 275 KPa en matrices con LP, de 100 a 360 KPa en componente de BPF y de 200-600 Kpa en matrices con TP. Así mismo fue encontrado que cuando disminuye la proporción de BPF y LP, los valores de IB aumentaron, siendo la mezcla 90:10 con 10% adhesivo con los valores de IB más altos. Pero las matrices con proporciones de TP, el valor IB es mayor en las proporciones con mayor proporción de este residuo, siendo la mezcla 50:50 con 10% las de mayor resistencia.