Polymer gel dosimeter based on itaconic acid

Abstract

A new polymeric dosimeter based on itaconic acid and N, N'-methylenebisacrylamide was studied. The preparation method, compositions of monomer and crosslinking agent and the presence of oxygen in the dosimetric system were analyzed. The resulting materials were irradiated with an X-ray tube at 158. cGy/min, 226. cGy. min and 298. cGy/min with doses up to 1000. Gy. The dosimeters presented a linear response in the dose range 75-1000. Gy, sensitivities of 0.037 1/Gy. at 298. cGy/min and an increase in the sensitivity with lower dose rates. One of the most relevant outcomes in this study was obtaining different monomer to crosslinker inclusion in the formed gel for the dosimeters where oxygen was purged during the preparation method. This effect has not been reported in other typical dosimeters and could be attributed to the large differences in the reactivity among these species.

Se estudió un nuevo dosímetro polimérico basado en ácido itacónico y N, N'-metilenbisacrilamida. Se analizaron el método de preparación, las composiciones de monómero y el agente de reticulación y la presencia de oxígeno en el sistema dosimétrico. Los materiales resultantes se irradiaron con un tubo de rayos X a 158 cGy / min, 226 cGy min y 298 cGy / min con dosis de hasta 1000 Gy. Los dosímetros presentaron una respuesta lineal en el rango de dosis 75–1000 Gy, sensibilidades de 0.037 1 / Gy a 298 cGy / min y un aumento en la sensibilidad con tasas de dosis más bajas. Uno de los resultados más relevantes en este estudio fue la obtención de diferentes monómeros para la inclusión de reticuladores en el gel formado para los dosímetros donde se purgó el oxígeno durante el método de preparación. Este efecto no se ha informado en otros dosímetros típicos y podría atribuirse a las grandes diferencias en la reactividad entre estas especies.